Tazipox · 2K epoxy resin
Tazipox EP120, 2K epoxy resin.
Heat-curing two-component (2K) epoxy resin. Pot life 60 min for a 100 g batch, curing in 90 min at 60 °C.
Technical data
- Viscosity of component A (resin) at 23 °C
- 8,000 mPa·s
- Viscosity of component B (hardener) at 23 °C
- 800 mPa·s
- Viscosity of mixture at 23 °C
- 4,800 mPa·s
- Density of component A (resin)
- 1.16 g/cm³
- Density of component B (hardener)
- 0.98 g/cm³
- Density of mixture
- 1.12 g/cm³
- Epoxy equivalent weight (EEW), component A (resin)
- 176.6 g/eq
- Amine hydrogen equivalent weight (AHEW), component B (hardener)
- 53.97 g/eq
- Modulus of elasticity
- > 4,000 MPa
- Flexural stress
- > 90 MPa
- Elongation at break
- 2.2 %
- Resistance to 10 % H₂SO₄, 30 days
- resistant
- Resistance to 1 % NaOH, 30 days
- resistant
- Glass transition Tg1 (cured at 60 °C for 2 h)
- 81 °C
- Glass transition Tg2 (second heating run)
- 150 °C
Values as per the technical data sheet. Binding values and the complete data sheet are available on request.
Processing
- System type
- 2K epoxy resin
- Mixing ratio (resin : hardener)
- 3 : 1
- Stoichiometric mixing ratio (A : B)
- 100 : 30.56
- Pot life (100 g, 21 °C to 40 °C)
- 60 min
- Working time (rolled out to 4 mm in the liner)
- 120 min
- Curing time at 60 °C
- 90 min
- Curing time at 80 °C
- 50 min
- Maximum temperature (100 g batch)
- 122 °C
- Heat-curing: cures at 60 °C or 80 °C, curing times in the technical data.
- Resin and hardener are mixed before processing.
- Adjustable pot life; we agree the mixing ratio and curing conditions with you during product development.
Documents
We send data sheets on request.
Other resins · Tazipox
01 / 2K epoxy resin
Tazipox EP30
Cold-curing; technical data and data sheet on request.
View product
02 / 2K epoxy resin
Tazipox EP60
Cold- or heat-curing: pot life 23 min, cures in 45 min at 60 °C.
View product
03 / 2K epoxy resin
Tazipox EP240
Heat-curing: pot life up to 240 min, cures in 150 min at 60 °C.
View product